SUMIKASUPER® LCP E7008
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKASUPER® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5gXFSG_SUMIKASUPER-LCP-E7008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.71 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.17 | % | |
| Across Flow | 1.1 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 127 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.2 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 11300 | MPa | |
| 200°C | 3230 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Yield, 23°C | 138 | MPa | |
| Yield, 200°C | 24.0 | MPa | |
| Shear Strength | 49.0 | MPa | ASTM D732 |
| Poisson's Ratio | 0.42 | ASTM E132 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.40 mm) | 56 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.40 mm) | 280 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 242 | °C | ASTM D648 |
| CLTE | Internal Method | ||
| Flow : 150°C | 8.0E-6 | cm/cm/°C | |
| Transverse : 150°C | 7.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.56 | W/m/K | JIS R2618 |
| RTI Elec (3.20 mm) | 130 | °C | UL 746 |
| RTI Imp (3.20 mm) | 130 | °C | UL 746 |
| RTI Str (3.20 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.70 | ||
| 1 MHz | 4.10 | ||
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 0.024 | ||
| 1 MHz | 0.030 | ||
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index | 155 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.380 mm) | V-0 | UL 94 | |
| Oxygen Index | 49 | % | JIS K7201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soldering Resistance | 275 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 320 to 340 | °C | |
| Nozzle Temperature | 320 to 340 | °C | |
| Processing (Melt) Temp | 320 | °C | |
| Mold Temperature | 70.0 to 160 | °C | |
| Injection Pressure | 78.0 to 157 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 to 39.0 | MPa | |
| Back Pressure | 0.980 to 4.90 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VPA780 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| XYRON™ X8610 | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| NEFTEKHIM PE 4028X (28435) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| AMTOPP BFP15 | Inteplast Group | PP, Unspecified | AMTOPP |
| Elastron® D D400.A50.N | Elastron USA, Inc. | SBS | Elastron® D |