INEOS PP R01A-00
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5fVyqd_INEOS-PP-R01A-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| R01A-00 is a low flow rate, antistatic polypropylene random copolymer. It is designed for blow molding, thermoforming and extrusion applications that require good stiffness and improved processability. Benefits of this grade include good see-through and contact clarity and good impact resistance at both room and refrigerator temperatures. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.9 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 76 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 28.1 | MPa | |
| Break | 21.9 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 13 | % | |
| Break | 680 | % | |
| Flexural Modulus - 1% Secant | 986 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 4°C | 37 | J/m | |
| 23°C | 85 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| 4°C | 3.60 | kJ/m² | |
| 23°C | 8.30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 133 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 93 | ASTM D2457 | |
| Haze 3(1270 µm) | 57 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P50B07/P50B07-S (Single Strand) | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| Sumikon® EME-6710HL | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Versalloy™ XL 9055X-9 | PolyOne Corporation | TPE | Versalloy™ |
| Optimum® 2014-XE | RAUH Polymers, Inc. | Copolyester | Optimum® |
| LNP™ THERMOCOMP™ MF001AS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |