CALIBRE™ IM 401-11
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5fPqkZ_CALIBRE-IM-401-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ IM 401-11 Impact Modified Polycarbonate resin is available in opaque formulations that offer benefits ranging from superior low temperature impact strength to easy processing with improved impact strength in highly filled formulations. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955, ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 55.8 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 130 | % | ASTM D638 |
| Break | 130 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 3 | 2280 | MPa | ASTM D790 |
| -- | 2270 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 4 | 89.6 | MPa | ASTM D790 |
| -- | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 690 | J/m | ASTM D256, ISO 180/4A |
| Instrumented Dart Impact 5(23°C, Total Energy) | 56.5 | J | ASTM D3763 |
| Tensile Impact Strength | 630 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648, ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 121 | °C | |
| 1.8 MPa, Annealed | 136 | °C | |
| Vicat Softening Temperature | 146 | °C | ISO 306/B50, ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 7 | UL 94 | ||
| 1.59 mm | HB | ||
| 3.20 mm | HB |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Method I (3 point load), 2.0 mm/min |
| 4 . | Method I (3 point load), 2.0 mm/min |
| 5 . | 3.39 m/sec |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID D 300 FV13 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 612 | MAZMID D |
| Ultramid® B36 | BASF Corporation | Nylon 6 | Ultramid® |
| Desmopan® DP 6064A | Covestro - PUR | TPU, Unspecified | Desmopan® |
| Elastron® V V201.A73.N | Elastron USA, Inc. | TPV | Elastron® V |
| Sumiliteresin® PR-50590 BI | SBHPP | Phenolic | Sumiliteresin® |