MARCOBLEND 7100
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | POLY GIN |
| Trademark: | MARCOBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5evVZd_MARCOBLEND-7100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| MARCOBLEND 7100 is an ignition resistant and glass fiber reinforced polycarbonate ABS resin. The resin is Halogen free and compliance with TCO and RoHS certification. The unique characters include superior processability, good stiffness, and excellent dimension stability and suitable for use in TFT LCD frame and internal structure parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (240°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 73.0 | MPa | ASTM D638 |
| Flexural Modulus | 3600 | MPa | ASTM D790 |
| Flexural Strength | 122 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow | 4.5E-5 | cm/cm/°C | |
| Transverse | 6.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 240 to 275 | °C | |
| Middle Temperature | 240 to 275 | °C | |
| Front Temperature | 240 to 275 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S359 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Tarnoform® 200 AR | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| DURANEX® 3300 | Polyplastics Co., Ltd. | PBT | DURANEX® |
| KIBITON® TPE PB-511 | CHI MEI CORPORATION | TPE | KIBITON® TPE |
| Huafon JF-PDY-511H | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |