Versaflex™ GP 2810-60N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Versaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5eMMpb_VersaflexGP281060N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Versaflex™G 7360 is an easy-to-process universal TPE designed for a wide range of applications, including applications that must comply with FDA standards.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 10 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | > 100 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 60 | DIN 53505 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504 | ||
| 100% strain, 2.00mm | 2.00 | MPa | DIN 53504 |
| 300% strain, 2.00mm | 3.00 | MPa | DIN 53504 |
| Tensile Strength 1(Break, 2.00 mm) | 5.50 | MPa | DIN 53504 |
| Tensile Elongation 2(Break, 2.00 mm) | 700 | % | DIN 53504 |
| Tear Strength (2.00 mm) | 25.0 | kN/m | ISO 34 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 32 | % | ISO 815 |
| 70°C, 22 hr | 52 | % | ISO 815 |
| 100°C, 22 hr | 72 | % | ISO 815 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 11200 sec^-1) | 8.00 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 160 - 188 | °C | |
| Middle Temperature | 177 - 193 | °C | |
| Front Temperature | 188 - 210 | °C | |
| Nozzle Temperature | 188 - 216 | °C | |
| Mold Temperature | 16 - 38 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.827 | MPa |
| Note Message | |
|---|---|
| 1 . | 2 hours |
| 2 . | 2 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® LX851C | Zeon Corporation | Latex | Nipol® |
| Geon™ BIO RA551S | PolyOne Corporation | PVC, Flexible | Geon™ BIO |
| Hylex® P2310L | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| LNP™ LUBRICOMP™ LGL33 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |
| EPALINE 393A34 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPALINE |