Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish.

General Information
Filler / Reinforcement	Long glass fiber, 60% filler by weight
Features	Thermal Stability
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.70	g/cm³	ISO 1183
Molding Shrinkage
--	0.17	%	ASTM D955
-- ¹	0.30	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
--	20500	MPa	ASTM D638
--	20000	MPa	ISO 527-2
Tensile Stress
Fracture	246	MPa	ASTM D638
Fracture	270	MPa	ISO 527-2
Tensile Strain
Fracture	1.9	%	ASTM D638
Fracture	2.0	%	ISO 527-2
Flexural Modulus
--	18300	MPa	ASTM D790
--	17000	MPa	ISO 178
Flexural Stress
--	401	MPa	ASTM D790
--	360	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	25	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	90	kJ/m²	ISO 179
Notched Izod Impact	260	J/m	ASTM D256
Dart Drop Impact	16.4	J	ASTM D5420

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	253	°C	ASTM D648
1.8 MPa, not annealed	254	°C	ISO 75-2/A
8.0 MPa, not annealed	241	°C	ISO 75-2/C

Flammability	Nominal Value	Unit	Test Method
Glow Wire Flammability Index (3.00 mm)	960	°C	IEC 60695-2-12

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	4.0	hr
Processing (Melt) Temp	290 - 320	°C
Mold Temperature	90.0	°C
Injection Rate	Slow-Moderate
Back Pressure	1.00	MPa

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.

Note Message
1 .	Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processing conditions.

Category:	Nylon 66 , Polyamide 66
Manufacturer:	PolyOne Corporation
Trademark:	OnForce™ LFT
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5e85DH_OnForce-LFT-NN-60LGF-000-HS-Natural.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Titalon® 1300CF	Titan Plastics Compounds Co., Ltd.	Nylon 6	Titalon®
Bolv LDPE 273-83	Shandong Jining Bolv Chemicals Co.,Ltd	LDPE	Bolv
Complet® LGF40-PEI	PlastiComp, Inc.	PEI	Complet®
OP - PC - Unfilled 912	Oxford Polymers	PC	OP - PC - Unfilled
RTP 2299 X 126107 A	RTP Company	PEEK	RTP