Infino TK-2046H
| Category: | PCT , Polycyclohexylenedimethylene Terephthalate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5dbhLW_Infino-TK-2046H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino TK-2046H is a Polycyclohexylenedimethylene Terephthalate (PCT) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 60 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.41 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.61 to 0.74 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5600 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/5 |
| Break 3 | 61.0 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | |||
| -- 5 | 7000 | MPa | ASTM D790 |
| -- 6 | 7000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 80.0 | MPa | ASTM D790 |
| -- 8 | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 25 | J/m | ASTM D256 |
| 23°C 10 | 2.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 281 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 260 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 260 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 to 3.00 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reflectance - Initial 11 | 90 | % | ASTM E1331 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 290 to 295 | °C | |
| Middle Temperature | 300 | °C | |
| Front Temperature | 305 to 310 | °C | |
| Nozzle Temperature | 310 | °C | |
| Mold Temperature | 130 to 160 | °C | |
| Injection Pressure | 120 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 4 mm |
| 10 . | Thickness: 4 mm |
| 11 . | Condition: At 440 NM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 4891 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| EVATHENE® UE653-04 | USI Corporation | EVA | EVATHENE® |
| Karina IVORY PVC COMPOUND -E 90850-35/1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| HiFill® PBT 0143 S | Techmer Engineered Solutions | PBT | HiFill® |
| POLYblend PC/ABS 45FS GKF2010 | Polykemi AB | PC+ABS | POLYblend |