TOTAL Polyethylene Lumicene® M 2310 EP
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5dGRim_TOTAL-Polyethylene-Lumicene-M-2310-EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M 2310 EP is a second generation metallocene based Linear Low Density Polyethylene with hexene as comonomer. Lumicene® mPE M 2310 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control and in comparison with conventional LLDPE and first generation metallocene based polyethylene. Lumicene® mPE M 2310 EP is especially dedicated to film applications where superior optical properties in combination with excellent impact resistance (even at low temperature) and sealing strength are required, particularly in blend and coextrusion with LLDPE or LDPE. Lumicene® mPE M 2310 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, deep freeze, collation shrink and lamination. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 40 µm, Blown Film | 12.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 59.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 58.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm, Blown Film | 650 | % | |
| TD : Break, 40 µm, Blown Film | 740 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 310 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 40.0 µm | 80.0 | kN/m | |
| TD | 165.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 114 | °C | ISO 306 |
| Melting Temperature | 116 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 73 | ASTM D2457 | |
| Haze 2(40.0 µm) | 5.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3970 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Next ABS SX-02AVBK | Next Polymers Ltd. | ABS | Next ABS |
| Karina CLEAR PVC COMPOUND -E 70/206-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MACOMASS PVC MM-PVC E 1561 | MACOMASS Verkaufs AG | PVC, Flexible | MACOMASS PVC |
| LNP™ STAT-LOY™ A30009 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |