Latilub 66-10T G/30-V0KB1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5cPfOk_Latilub-66-10T-G-30-V0KB1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Polyamide 66 (PA 66). PTFE. Glass fibres. UL94 V-0 classified, with red phosphorous. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 1.0 | % | |
| Flow : 2.00 mm | 0.35 to 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 9900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 165 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.9 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.30 | ||
| vs. Itself - Static | 0.35 | ||
| Wear Factor | 2.10E-9 | (m³/h)/(N·m·h) | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 265 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 255 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 825 | °C | |
| 2.00 mm | 825 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Qenos PP PPW 1780 | Qenos Pty Ltd | PP Homopolymer | Qenos PP |
| Nanjing Hongrui PP P304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| Compoceran E102B | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |
| EMERGE™ PC 4330-10 | Trinseo | PC | EMERGE™ |
| Durethan® BKV 315 Z H2.0 901510 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |