Braskem PE GP100ORXP
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5cEPh7_BraskemPEGP100ORXP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GP100ORXP is a High Density Polyethylene compound specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal technology and has high molar mass. It shows excellent mechanical properties and resistance to hydrostatic pressure and stress cracking. This resin has MRS (Minimum Required Strength) of 10 MPa, according to ISO 9080, and is classified as PE 100, according to ISO 12162. GP100ORXP is manufactured in orange color and contains additives to protect it against ultraviolet radiation action and photodegradation. Meets the requirements of NBR 14462:00 and ISO 4437:07. Application: Orange PE 100 pressure pipes for gas distribution; jacketing of underwater cables Process: Pipe Extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 2.00mm, 10% Igepal, molded, F50 | > 1000 | hr | ASTM D1693 |
| 50°C, 2.00mm, 100% Igepal, molded, F50 | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 24.0 | MPa | ASTM D638 |
| Fracture, molding | 38.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, molding | 10 | % | ASTM D638 |
| Fracture, molding | 1500 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 1050 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 69.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 5502-UV | Colorite Polymers | PVC, Unspecified | Unichem |
| ZELAS® MC715R4 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | ZELAS® |
| CP PRYME® Nylon 66 NN100HSL | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Sylvin 3290-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ QF00A compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |