| Novodur Ultra 4105 is a PC modified high heat injection molding grade with high impact strength. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 9.00 | cm³/10min | |
| 260°C/5.0 kg | 12.0 | cm³/10min | |
| Molding Shrinkage | 0.60 to 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 85.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 45.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 3.7 | % | |
| Break, 23°C | > 15 | % | |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 34 | kJ/m² | |
| 23°C | 42 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 108 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 106 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength 1(1.50 mm) | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 4.0E-3 | ||
| 1 MHz | 8.5E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 240 | mm/sec |
| Note Message | |
|---|---|
| 1 . | Short Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ H14HT | Mando Advanced Materials Co., Ltd. | ABS+Nylon | TEKAMID™ |
| ALCOM® PA6 900/1 GF15 GB15 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Formolene® 6610A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Formolene® 5102KR | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Sylvin 5215-88FRUV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |