SABIC® LDPE 1922N0
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5aNrgp_SABIC-LDPE-1922N0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 1922N0 is an additive free LDPE grade produced by SABIC's CTR® tubular technology. This grade is typically developed for food contact applications that require high product quality, consistency and high level of purity. SABIC will offer for SABIC® LDPE 1922N0 the full food compliance service package. Application. SABIC® LDPE 1922N0 is typically suitable for applications that require a good balance between flow properties and mechanical properties. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 22 | g/10 min | |
| 190°C/5.0 kg | 75 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 29.0 | cm³/10min | |
| 190°C/5.0 kg | 98.0 | cm³/10min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 40 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 175 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 8.00 | MPa | |
| Break, 2.00 mm, Compression Molded | 7.00 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | 400 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus 1 | ISO 899-1 | ||
| 1 hr | 80.0 | MPa | |
| 1000 hr | 45.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 5.0 | kJ/m² | |
| 23°C, Compression Molded | 42 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 39.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 82.0 to 83.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 105 to 107 | °C | DIN 53765 |
| Enthalpy Change | 104 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AXELERON™ CS L-3364 NT CPD | The Dow Chemical Company | HDPE | AXELERON™ |
| Ebalta MG 707 / Z 400 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| EMPILON® HB60 | EMPILON | SEBS | EMPILON® |
| HiFill® PBT GF30 | Techmer Engineered Solutions | PBT | HiFill® |
| Karina CLEAR PVC COMPOUND -E 80/200-SI-CRMT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |