Polylink Polymer PBT-11020-GF
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polylink Polymers (India) Ltd. |
| Trademark: | Polylink Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5X7fam_Polylink-Polymer-PBT-11020-GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Filled PBT compounds are manufacturedbycom pounding PBT with specially treated choppedglass and modified with additives to make parts withhigh mechanical properties, heat resistance and fire resistance.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 - 1.60 | g/cm³ | Internal method |
| Moisture Content | < 800 | ppm | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 88.3 - 98.1 | MPa | ASTM D638 |
| Flexural Modulus | 5490 - 5690 | MPa | ASTM D790 |
| Flexural Strength | 147 - 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 49 - 54 | J/m | ASTM D256 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 215 | °C | |
| Cylinder Zone 2 Temp. | 220 | °C | |
| Cylinder Zone 3 Temp. | 230 | °C | |
| Cylinder Zone 4 Temp. | 240 | °C | |
| Cylinder Zone 5 Temp. | 245 | °C |
| Extrusion instructions |
|---|
| Zone 6 : 250°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nilac TR F17 | Soredi S.p.a. | ABS | Nilac |
| ADMER™ NF408E | Mitsui Chemicals Europe GmbH | PE, Unspecified | ADMER™ |
| Latilub 87/28-15T K/20 | LATI S.p.A. | PC | Latilub |
| Karina COMP. PVC BLACK -E KAPU 6048/ 1D | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| RTP 702 CC | RTP Company | HDPE | RTP |