PermaStat® 105
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | PermaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5WW8YM_PermaStat-105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4480 | MPa | ASTM D638 |
| Tensile Strength | 52.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 4130 | MPa | ASTM D790 |
| Flexural Strength | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 370 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Tensile Elongation, ASTM D 638: 3-6%Volume Resistivity, ASTM D 257: 1000000000 - 10000000000 ohm-cmSurface Resistivity, ASTM D 257: 10000000000 - 100000000000 ohm/sqStatic Decay, FTMS-4046.1, Mil B-81705C: <2.0 seconds |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 182 - 204 | °C | |
| Middle Temperature | 182 - 204 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Mold Temperature | 32.2 - 65.6 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO S1005 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| ADENE BCWB | A.D. Compound spa | PP Homopolymer | ADENE |
| MAJORIS PBT 9237 3030 FB BLACK 8229 | AD majoris | PBT | MAJORIS |
| TOTAL Polyethylene Lumicene® M 3423 UV black | TOTAL Refining & Chemicals | mMDPE | TOTAL Polyethylene |
| PSM® HL-103 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |