TEKNIFLEX® COC P10P
| Category: | Film, PP/COC/PP , PP/COC/PP Film |
| Manufacturer: | Tekni-Films, a div of Tekni-Plex |
| Trademark: | TEKNIFLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5WSGiG_TEKNIFLEX-COC-P10P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoformable, FDA-compliant, Pharmaceutical-Grade Cyclic Olefine Copolymer film. Tekni-Plex offers a wide range of polyolefin-based film structures to meet both performance and cost requirements. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.00 | g/cm³ | |
| Dimensional Stability 1(140°C) | -3.0 to 3.0 | % |
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Film Thickness 2 | 300 | µm | |
| Yield | 3.34 | m²/kg |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Roll Width 3 | < 110.00 | cm | |
| Thermoforming Molding Temperature | 120 to 160 | °C |
| Films | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength - MD (Yield) | 21.0 | MPa | |
| Oxygen Transmission Rate (23°C, 100% RH) | 110 | cm³/m²/24 hr | |
| Water Vapor Transmission Rate (38°C, 90% RH) | 0.28 | g/m²/24 hr |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Haze | 15 | % |
| Note Message | |
|---|---|
| 1 . | 30 minutes |
| 2 . | Thickness tolerance: ±10% |
| 3 . | Roll width tolerance: ±1.5 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-80A-B30 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| NEXT REGRIND PBT DR51-300RG | NEXT Specialty Resins, Inc. | PBT | NEXT REGRIND |
| ALFATER XL® D50E 1GP0001 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| EVICOM™ GA6/266 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| KEBAFLEX® U A 85 EF B01 natural | BARLOG plastics GmbH | TPU, Unspecified | KEBAFLEX® |