Diakon® CM12515
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5WQRKx_Diakon-CM12515.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diakon® CM12515 is a Polymethyl Methacrylate Acrylic material. It is available in Europe for injection molding. Primary attribute of Diakon® CM12515: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ISO 2039-2 | |
| Ball Indentation Hardness (H 961/30) | 175 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 18 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 1.7 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 91.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 88.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ISO 306/A |
| -- | 93.0 | °C | ISO 306/B |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 0.40 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Hopper Temperature | 50.0 to 80.0 | °C | |
| Rear Temperature | 180 to 230 | °C | |
| Middle Temperature | 210 to 260 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN HSG-372 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| TIPOLEN® FD 243-51 | MOL Petrochemicals Co. Ltd. | LDPE | TIPOLEN® |
| Infino WP-1041 | SAMSUNG SDI CO., LTD. | PC+ABS | Infino |
| LUVOCOM® 20-8333 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| TECHNYL® C 236 V35 BLACK Z | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |