PTS PCA-1012
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polymer Technology and Services, LLC |
| Trademark: | PTS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5UdciM_PTS-PCA-1012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PTS PCA-1012 is a Polycarbonate + ABS (PC+ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (3.17 mm) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.17 mm) | 130 | % | ASTM D638 |
| Flexural Modulus (3.17 mm) | 2210 | MPa | ASTM D790 |
| Flexural Strength (3.17 mm) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.17 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 102 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm, NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Shot Size | 50 to 80 | % | |
| Rear Temperature | 221 to 229 | °C | |
| Middle Temperature | 224 to 235 | °C | |
| Front Temperature | 229 to 241 | °C | |
| Nozzle Temperature | 232 to 243 | °C | |
| Processing (Melt) Temp | 238 to 254 | °C | |
| Mold Temperature | 68.3 to 87.8 | °C | |
| Injection Pressure | 68.9 to 138 | MPa | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 6019 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Random Copolymer | POLYPRO® |
| PrimoFlo 90A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| EEC LLD 3505 U | Egyptian European Company | PE, Unspecified | EEC |
| POLYCOMPO PP J229E | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| LNP™ LUBRICOMP™ LX91475 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |