Generic TPO (POE)
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5UGtUM_Generic-TPO-POE-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPO (POE) This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.857 - 1.05 | g/cm³ | ASTM D792 |
| 23°C | 0.880 - 0.985 | g/cm³ | ISO 1183 |
| -- | 0.862 - 0.887 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.090 - 20 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.50 - 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.2 - 2.5 | % | ASTM D955 |
| 23°C | 0.40 - 1.6 | % | ISO 294-4 |
| Mooney Viscosity | 2 - 38 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 11 - 96 | ASTM D2240 | |
| 23°C | 32 - 99 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1.21 - 34.9 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 4.20 - 230 | MPa | ASTM D638 |
| Yield, 23°C | 9.90 - 21.1 | MPa | ISO 527-2 |
| Fracture, 23°C | 1.30 - 27.9 | MPa | ASTM D638 |
| 23°C | 0.900 - 21.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 5.0 - 300 | % | ASTM D638 |
| Yield, 23°C | 6.9 - 15 | % | ISO 527-2 |
| Fracture, 23°C | 10 - 1000 | % | ASTM D638 |
| Fracture, 23°C | 490 - 510 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1.20 - 626 | MPa | ASTM D790 |
| 23°C | 20.0 - 2850 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| 100% strain, 23°C | 1.24 - 6.99 | MPa | ASTM D412 |
| 100% strain, 23°C | 1.70 - 11.3 | MPa | ISO 37 |
| 300% strain, 23°C | 3.03 - 12.6 | MPa | ASTM D412 |
| Tensile Strength | |||
| Yield, 23°C | 3.62 - 12.4 | MPa | ASTM D412 |
| Fracture, 23°C | 2.40 - 21.3 | MPa | ASTM D412 |
| Fracture, 23°C | 8.45 - 15.4 | MPa | ISO 37 |
| Tensile Elongation | |||
| Yield | 200 - 500 | % | ASTM D412 |
| Fracture, 23°C | 240 - 810 | % | ASTM D412 |
| Fracture, 23°C | 520 - 880 | % | ISO 37 |
| Tear Strength | |||
| 23°C | 14.3 - 113 | kN/m | ASTM D624 |
| 23°C | 80 - 120 | kN/m | ISO 34-1 |
| Compression Set | 15 - 79 | % | ASTM D395 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 3.5 - 40 | J/m | ASTM D256 |
| 23°C | 23 - 61 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 16.0 - 19.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 12.2 - 136 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 53.0 - 106 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 37.0 - 57.3 | °C | ISO 75-2/A |
| Brittleness Temperature | |||
| -- | -75.0 - -19.0 | °C | ASTM D746 |
| -- | -60.0 | °C | ISO 812 |
| Glass Transition Temperature | |||
| -- | -58.3 - -54.8 | °C | ASTM E1356 |
| -- | -59.2 - -30.2 | °C | DSC |
| Vicat Softening Temperature | 34.4 - 97.6 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 34.0 - 106 | °C | ISO 3146 |
| Peak Crystallization Temperature (DSC) | 13.0 - 90.0 | °C | ASTM D3418 |
| CLTE - Flow | |||
| -- | 4.8E-5 - 1.0E-4 | cm/cm/°C | ASTM E228 |
| -- | 4.0E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 105 - 115 | °C | UL 746 |
| RTI Imp | 105 - 115 | °C | UL 746 |
| RTI | 105 - 115 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 - 2.5E+10 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+2 - 2.5E+14 | ohms·cm | ASTM D257 |
| Dielectric Constant (23°C) | 2.10 - 2.43 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 25 - 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.3 - 79.6 | °C | |
| Drying Time | 1.9 - 3.5 | hr | |
| Rear Temperature | 159 - 206 | °C | |
| Middle Temperature | 169 - 216 | °C | |
| Front Temperature | 179 - 215 | °C | |
| Nozzle Temperature | 189 - 211 | °C | |
| Processing (Melt) Temp | 196 - 222 | °C | |
| Mold Temperature | 34.9 - 46.1 | °C | |
| Injection Pressure | 4.14 - 104 | MPa | |
| Back Pressure | 0.259 - 1.36 | MPa | |
| Screw Speed | 53 - 150 | rpm | |
| Cushion | 14.5 - 14.6 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPO (POE)This information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 165 - 178 | °C | |
| Cylinder Zone 2 Temp. | 175 - 182 | °C | |
| Cylinder Zone 3 Temp. | 180 - 188 | °C | |
| Cylinder Zone 4 Temp. | 185 - 186 | °C | |
| Cylinder Zone 5 Temp. | 193 - 212 | °C | |
| Melt Temperature | 195 - 205 | °C | |
| Die Temperature | 200 - 232 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPO (POE)This information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yanshan PE 5300B | SINOPEC Beijing Yanshan Petrochemical | HDPE | Yanshan PE |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| ADEKA SC,SP series | Adeka Corporation | PUR-Ether | ADEKA |
| Dialon 1015GK20 | DTR S.r.l. (Develop Thermoplastic Resins) | PC | Dialon |
| Flexoprene® 85 | Puma Tecnica S.A.I.C.F.I | PE, Unspecified | Flexoprene® |