CERTENE™ HPB-0354A
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5U4SaU_CERTENE-HPB-0354A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HPB-0354A is a certified prime Phillips Process blow molding copolymer designed to meet end-use requirements of containers for packaging of Household Industrial Chemicals (HIC). HPB-0354A contains antistatic and features medium swell, easy and consistent processability in conventional continuous or intermittent extrusion equipment, and excellent balance of bottle ESCR, Impact strength and Stiffness. Applications include medium size containers for detergents, bleach, antifreeze, motor oil and ice chests. HPB-0354A recommended processing temperature is 160 to 180°C, with mold at 10 to 30°C. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, Compression Molded, F50) | 50.0 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 700 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Compression Molded) | 1170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 206 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 74.0 | °C | ASTM D648 |
| Brittleness Temperature | -90.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Additional Information |
|---|
| This Specimen was compression molded and was tested according to ASTM D1928 Procedure C. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 10.0 - 30.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® CLEAR C 170 MED | Arkema | Nylon 11 | Rilsan® |
| New-prene™ 8280B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Novalloy-B B4720 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| POFEX EP8004S125V | POLYROCKS CHEMICAL CO., LTD | XLPE | POFEX |
| Sylvin 6247-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |