Order Products : sales@su-jiao.com
Nypol® PA C3 K82 HL NTLA010 NS305 MSP
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5QRKuW_Nypol-PA-C3-K82-HL-NTLA010-NS305-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Blends of polyamide 6.6 / 6 natural, good set of mechanical properties, high tenacity and elongation, excellent impact resistance and excellent surface finish. Ideal for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.3 to 1.6 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr 1 | 8.5 | -- | % | |
| 24 hr 2 | 1.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 60.0 to 95.0 | 50.0 to 55.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 35 | 400 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 50.0 | -- | J/m | ISO 179 |
| Notched Izod Impact | 50 | 1700 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 190 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 68.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 242 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+12 | 1.0E+11 | ohms·cm | ASTM D257 |
| Electric Strength | 26 | 32 24 | kV/mm | IEC 60243-1 |
| Dissipation Factor (1 MHz) | 0.031 | -- | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.700 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Saturation |
| 2 . | Immersion |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PE HDPE-0147 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| AKROMID® B3 GF 15 4 RM-M black (3440) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Elastron® V V101.A60.B | Elastron USA, Inc. | TPV | Elastron® V |
| Karina IVORY PVC COMPOUND IRDB 40-LF-BR(CABELAUTO) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pier One PC/ABS SF2000 BK10 | Pier One Polymers, Inc. | PC+ABS | Pier One PC/ABS |