LNP™ THERMOCOMP™ UF008AS compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5PU5v0_LNP-THERMOCOMP-UF008AS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UF008AS is a compound based on Polyphthalamide resin, containing Glass Fiber. Added features include; Mold Release. Also known as: LNP* THERMOCOMP* Compound UF-1008 A Product reorder name: UF008AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.14 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 234 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 12000 | MPa | ISO 178 |
| Flexural Stress | 315 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 55 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.3E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 320 | °C | |
| Middle Temperature | 315 to 325 | °C | |
| Front Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | 315 to 330 | °C | |
| Mold Temperature | 140 to 165 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® A30B041 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| Hanwha Total PP FB51 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina WHITE PVC COMPOUND 651D10/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID A GV25 H UV natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| Romiloy® 9130 | ROMIRA GmbH | PC+ABS | Romiloy® |