CABELEC® CA3817
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Cabot Corporation |
| Trademark: | CABELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5P5AcV_CABELEC-CA3817.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CABELEC® 3817 is an electrically conductive compound based on conductive carbon black and a modified linear low density polyethylene resin. Its electrical and mechanical properties are permanent and are not dependent on atmospheric conditions. CABELEC 3817 is recommended for packaging and product handling applications where freedom from the hazard of electrostatic discharge is necessary. Examples of use are in handling of explosive powders, pigments and electronic components. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.04 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) 2 | ISO 1133 | ||
| 190°C/10.0 kg | 6.0 | g/10 min | |
| 190°C/5.0 kg | 2.0 | g/10 min |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 3(Compression Molded) | 284 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | ISO 527-3/500 | ||
| MD : Yield, 100 µm | 11.8 | MPa | |
| TD : Yield, 100 µm | 11.5 | MPa | |
| MD : 100 µm | 25.1 | MPa | |
| TD : 100 µm | 22.4 | MPa | |
| Tensile Elongation 5 | ISO 527-3/500 | ||
| MD : Break, 100 µm | 1100 | % | |
| TD : Break, 100 µm | 940 | % | |
| Trouser Tear Resistance | ASTM D1938 | ||
| MD : 50 µm | 106 | N/mm | |
| TD : 50 µm | 104 | N/mm |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 6(0.100 mm) | 1.0E+4 | ohms | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 to 230 | °C | |
| Cylinder Zone 2 Temp. | 200 to 230 | °C | |
| Cylinder Zone 3 Temp. | 200 to 230 | °C | |
| Cylinder Zone 4 Temp. | 200 to 230 | °C | |
| Cylinder Zone 5 Temp. | 200 to 230 | °C | |
| Die Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | CTM E023 |
| 2 . | CTM E005 |
| 3 . | CTM E040A |
| 4 . | CTM E041 |
| 5 . | CTM E041 |
| 6 . | CTM E042B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMLLOY PA917G6 | Polyram Ram-On Industries | Nylon 66+PP | RAMLLOY |
| Mirakutoran® TPU P490 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sindustris PBT TE5101 | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| Karina YELLOW PVC COMPOUND 450-DA-02/ 21-ATB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polyrocks 7001C | Polyrocks Chemical Co., Ltd | ABS | Polyrocks |