ICORENE® 3940
| Category: | LLDPE , Linear Medium Density Polyethylene |
| Manufacturer: | ICO Polymers NA, A Division of A. Schulman |
| Trademark: | ICORENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5NaoNi_ICORENE3940.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ICORENE® 3940 is a linear low density polyethylene specifically developed for rotational moulding. ICORENE® 3940 is suitable for use in general purpose applications. It has a good balance of properties such as toughness and stiffness. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal) | 45.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 400 | % | ASTM D638 |
| Flexural Modulus | 730 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drop Impact Resistance 1(-20°C) | 170 | J/cm | Internal method |
| Note Message | |
|---|---|
| 1 . | Based on ISO 6603 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Megalon® 230L-BK | Mega Polymers | Nylon 6 | Megalon® |
| Sinpolene MBB3131 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| Fortron® FX4382T1 | Celanese Corporation | PPS | Fortron® |
| Hytrel® HTR237BG BK320 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Petro Rabigh PP AR764 | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |