ebalta LH 30is a two components epoxy laminating resin, precuring at room temperature and, depending on postcuring, can be used till 175°C. Since this laminating resin system contains no fillers, it has got good wetting properties and makes a high glass fabric content possible. This leads to a low coefficient of thermal expansion and high strength. Together with aluminium granules, ebalta LH 28-1 is suitable for back filling of heat resistant moulds and moulding tools. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 to 91 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2850 to 3350 | MPa | ISO 178 |
| Flexural Stress | 62.0 to 74.0 | MPa | ISO 178 |
| Compressive Stress | 90.0 to 110 | MPa | ISO 604 |
| Flexural Strain at Flexural Strength | 2.2 to 2.6 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 3.5 to 5.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 176 to 186 | °C | ISO 75-2/B |
| Glass Transition Temperature | 200 | °C | TMA |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 42 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time | |||
| 40°C | 4.0 to 6.0 | hr | |
| 60°C | 4.0 to 6.0 | hr | |
| 100°C | 4.0 to 6.0 | hr | |
| 150°C | 4.0 to 6.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.06 to 1.10 | g/cm³ | |
| Viscosity (25°C) | 1.7 to 2.7 | Pa·s | |
| Curing Time (20°C) | > 48 | hr | |
| Pot Life 1(20°C) | 160 to 200 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Proteus® Black | Quadrant Engineering Plastic Products | PP Homopolymer | Quadrant EPP |
| Milastomer™ 8051BS | Mitsui Chemicals America, Inc. | TPV | Milastomer™ |
| Baytec® SPR-186A | Covestro - PUR | PUR-Ether/MDI | Baytec® |
| Halene H R5801 | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| Sylvin 9077-70 Grey 9534 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |