DOW鈩?Adhesive Film (DAF) 780

Category:	Polyolefin, Unspecified , Polyolefin Adhesive Film
Manufacturer:	The Dow Chemical Company
Trademark:	DOW鈩?Adhesive Film (DAF)
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5Mbgz5_DOW-Adhesive-Film-DAF-780.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
DOW™ Adhesive Film (DAF) 780 is a low melt point, coextruded film used to improve slip characteristics of polyurethane foam for carpet installation or other applications. New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative. Heat Activation Point: 215°F (102°C) Yield: 208 ft²/lb/mil (42.6 m²/kg/25 µm) Available Colors: Red, blue, yellow, gray & clear Gauge Range: 0.6-0.9 mil (15-22.5 µm) Width Range: 50-75 in (1270-1905 mm)

Message

DOW™ Adhesive Film (DAF) 780 is a low melt point, coextruded film used to improve slip characteristics of polyurethane foam for carpet installation or other applications.

New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative.

Heat Activation Point: 215°F (102°C)

Yield: 208 ft²/lb/mil (42.6 m²/kg/25 µm)

Available Colors: Red, blue, yellow, gray & clear

Gauge Range: 0.6-0.9 mil (15-22.5 µm)

Width Range: 50-75 in (1270-1905 mm)

General Information
Appearance	Blue Clear/Transparent Grey Red Yellow
Forms	Film

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	19	µm
Film Thickness - Recommended / Available	0.6-0.9 mil (15-22.5 µ)
Secant Modulus			ASTM D882
2% Secant, MD : 19 µm	138	MPa
2% Secant, TD : 19 µm	159	MPa
Tensile Strength			ASTM D882
MD : Yield, 19 µm	15.9	MPa
TD : Yield, 19 µm	8.96	MPa
MD : Break, 19 µm	17.9	MPa
TD : Break, 19 µm	12.4	MPa
Tensile Elongation			ASTM D882
MD : Break, 19 µm	300	%
TD : Break, 19 µm	500	%
Elmendorf Tear Strength			ASTM D1922
MD : 19 µm	23	g
TD : 19 µm	340	g
Film Width	127.00 to 190.50	cm
Yield (25.0 µm)	42.6	m²/kg

Thermal	Nominal Value	Unit
Heat Activation Temperature	102	°C

Resin Grade	Manufacturer	Category	Trademark
Polypropylene C7038-38NA	Trinseo	PP Impact Copolymer	Polypropylene
WPP PP PPC3GF2.5-Natural	Washington Penn Plastic Co. Inc.	PP Impact Copolymer	WPP PP
HiFill® HIPS BK	Techmer Engineered Solutions	PS (HIPS)	HiFill®
LUVOCOM® 1/GF/20/TF/10/SI/2/BK	Lehmann & Voss & Co.	Nylon 66	LUVOCOM®
3M™ Dyneon™ Perfluoroelastomer PFE 40Z	3M Advanced Materials Division	Perfluoroelastomer	3M™ Dyneon™ Perfluoroelastomer