HIGH TRANSPARENCY ZeonorFilm exhibits high transparency (92% light transmittance) and excellent turbidity (haze value <0.1%), for enhanced brightness. INERT SURFACE ZeonorFilm is manufactured from Zeon's cyclo olefin polymer (COP). COP is known for its excellent optical properties and also for being a high-purity resin. ZeonorFilm has an inert surface which makes it ideal for sensitive bio-diagnostic devices. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | JIS K6760 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 120°C, 0.100 mm | 0.060 | % | |
| Flow : 120°C, 0.100 mm | -0.020 | % | |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | B | JIS K5401 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abbe Number (25°C) | 56.0 | ASTM D542 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Across Flow : 0.100 mm | 59.0 | MPa | |
| Flow : 0.100 mm | 60.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Across Flow : Break, 0.100 mm | 30 | % | |
| Flow : Break, 0.100 mm | 40 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 136 to 163 | °C | DSC |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (0.0100 mm) | 360 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 | |
| Arc Resistance (3.00 mm) | 124 | sec | ASTM D495 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 1 | 1.530 | ASTM D542 | |
| Transmittance (100 µm) | 92.0 | % | JIS K7105 |
| Haze (100 µm) | < 0.10 | % | JIS K7105 |
| Note Message | |
|---|---|
| 1 . | D line, 25°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tislamid® PA66 PA66 30 GFR EP | Tisan | Nylon 66 | Tislamid® PA66 |
| Baoding 67I85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| HiFill® PA6/6 GF33 LE | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Sylvin 9940-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® BFN 4231 000000 | LANXESS GmbH | PBT | POCAN® |