HYPERTHERM™ 2399 NT
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | HYPERTHERM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5MHP30_HYPERTHERM-2399-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HYPERTHERM -2399 NT BIMODAL POLYETHYLENE Resin is a Polyethylene resin with raised temperature capability produced using UNIPOL II process technology. This product is intended for use in piping systems where high temperatures and aggressive oxidation conditions exist. Suitable applications include hot and cold potable water. Industrial Standards Compliance: ASTM D 3350: cell classification PE445574A Plastics Pipe Institute (PPI): TR-4
Meets requirements of
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (Natural) | 0.950 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | > 24.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1050 | MPa | ASTM D790B |
| resistant to rapid crack propagation, Pc- S-4 (0°C) 3 | > 12.0 | bar | ISO 13477 |
| resistant to rapid crack propagation, Tc- S-4 @ 145 psi (10 bar) 4 | °C | ISO 13477 | |
| Slow crack propagation PENT- @ 2.4 MPa 5 | ASTM F1473 | ||
| 80°C | > 12000 | hr | ASTM F1473 |
| 90°C | > 6000 | hr | ASTM F1473 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability | > 220 | °C | ASTM D3350 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Chlorine Resistance Level | 5.00 | ASTM F2023/F2769 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 490 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 7 | < -75.0 | °C | ASTM D746A |
| Melting Temperature (DSC) | 132 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 232 | °C |
| Extrusion instructions |
|---|
| Fabrication Conditions: Screw Type: High quality HDPE barrier with mixing Melt Temperature Range: 380-450°F (193-232°C) |
| Note Message | |
|---|---|
| 1 . | Compression molded parts prepared according to ASTM D 1928 Procedure C. Properties will vary with changes in molding conditions and aging time. |
| 2 . | Compression molded parts prepared according to ASTM D 1928 Procedure C. Properties will vary with changes in molding conditions and aging time. |
| 3 . | The pipe diameter is 10 inches IPS (25.4cm) and the standard diameter ratio (SDR) is 11. |
| 4 . | Pipe diameter of 10 inch IPS (25.4 cm) and Standard Diameter Ratio (SDR) 11. |
| 5 . | Compression molded parts prepared according to ASTM D 1928 Procedure C. Properties will vary with changes in molding conditions and aging time. |
| 6 . | Compression molded parts prepared according to ASTM D 1928 Procedure C. Properties will vary with changes in molding conditions and aging time. |
| 7 . | Compression molded parts prepared according to ASTM D 1928 Procedure C. Properties will vary with changes in molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4780 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sanren Y180L (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| SumiDurez 110 | SumiDurez Singapore Pte Ltd | Phenolic | SumiDurez |
| Colorite Rigid PVC 2401H | Colorite Polymers | PVC, Rigid | Colorite Rigid PVC |
| Elvacite® 2014 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |