| Prime Polypro™ J-2000GP is a Polypropylene Homopolymer (PP Homopolymer) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: homopolymer. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.4 to 1.8 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 33 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 50 | % | ISO 527-2 |
| Flexural Modulus | 1450 | MPa | ISO 178 |
| Flexural Stress | 42.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 3.1 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 93.0 | °C | ISO 75-2/B |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 80 | ASTM D2457 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech B9260 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| SUPREME HIPS SH2157 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| TRIBIT® 1500G15 | Samyang Corporation | PBT | TRIBIT® |
| KOPA® KN333HB40HFBL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| LNP™ THERMOCOMP™ RF00AH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |