VALOX™ 310SE0 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Kt9fS_VALOX-310SE0-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VALOX 310SE0 is an unreinforced, flame retardant PBT injection moulding resin. Applications: electrical industry, bobbins, keyboard, switches and switch components and appliance housings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.710 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.6 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 1.1 to 1.8 | % | |
| Flow 2 | 1.5 to 2.3 | % | |
| Flow 3 | 0.90 to 1.6 | % | |
| Flow : 3.20 mm | 1.5 to 2.3 | % | |
| Across Flow 4 | 0.90 to 1.9 | % | |
| Across Flow 5 | 1.0 to 1.7 | % | |
| Across Flow 6 | 1.6 to 2.4 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.36 | % | |
| Equilibrium, 23°C, 50% RH | 0.080 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 105 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 7 | 2820 | MPa | ASTM D638 |
| -- | 2800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 8 | 58.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 9 | 58.0 | MPa | ASTM D638 |
| Break | 40.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 10 | 20 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 11 | 20 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 12 | 2620 | MPa | ASTM D790 |
| -- 13 | 2600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 14 | 101 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 19.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 15 | 4.0 | kJ/m² | ISO 179/1eA |
| 23°C 16 | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 17 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -30°C | 22 | J/m | ASTM D256 |
| 23°C | 37 | J/m | ASTM D256 |
| -30°C 18 | 3.0 | kJ/m² | ISO 180/1A |
| 23°C 19 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| -30°C 20 | No Break | ISO 180/1U | |
| 23°C 21 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 200 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 162 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 100 mm Span 22 | 135 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 74.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 71.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 23 | 60.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, Unannealed, 64.0 mm Span 24 | 71.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 165 | °C | ASTM D1525, ISO 306/B50, ISO 306/B120 25 |
| -- | 212 | °C | ISO 306/A50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : 60 to 138°C | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 7.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : 23 to 60°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.24 | W/m/K | ISO 8302 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 1.60 mm, in Oil | 22 | kV/mm | ASTM D149 |
| 3.20 mm, in Air | 18 | kV/mm | ASTM D149 |
| 0.800 mm, in Oil | 31 | kV/mm | IEC 60243-1 |
| 1.00 mm 26 | 18 | kV/mm | IEC 60243-1 |
| 1.60 mm, in Oil | 24 | kV/mm | IEC 60243-1 |
| 3.20 mm, in Oil | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | ||
| 60 Hz | 2.90 | ||
| 100 Hz | 3.10 | ||
| 1 MHz | 2.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | ||
| 60 Hz | 1.0E-3 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 0.010 | ||
| Arc Resistance 27 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 175 | V | |
| Solution B | 100 | V | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) | PLC 6 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 232 to 249 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 243 to 260 | °C | |
| Nozzle Temperature | 238 to 254 | °C | |
| Processing (Melt) Temp | 243 to 260 | °C | |
| Mold Temperature | 48.9 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.3 to 4.6 mm |
| 3 . | 0.75 to 2.3 mm |
| 4 . | Tensile Bar |
| 5 . | 0.75 to 2.3 mm |
| 6 . | 2.3 to 4.6 mm |
| 7 . | 5.0 mm/min |
| 8 . | Type I, 50 mm/min |
| 9 . | Type I, 50 mm/min |
| 10 . | Type I, 50 mm/min |
| 11 . | Type I, 50 mm/min |
| 12 . | 1.3 mm/min |
| 13 . | 2.0 mm/min |
| 14 . | 1.3 mm/min |
| 15 . | 80*10*4 sp=62mm |
| 16 . | 80*10*4 sp=62mm |
| 17 . | 80*10*4 sp=62mm |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 |
| 20 . | 80*10*4 |
| 21 . | 80*10*4 |
| 22 . | 120*10*4 mm |
| 23 . | 120*10*4 mm |
| 24 . | 80*10*4 mm |
| 25 . | Rate B (120°C/h), Loading 2 (50 N) |
| 26 . | Short-Time |
| 27 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 226F7 | SAX Polymers | Nylon 66 | SAXAMID™ |
| NEFTEKHIM PE 6254N | Nizhnekamskneftekhim Inc. | HDPE | NEFTEKHIM PE |
| Hostacom Premium TBC 141N | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| POLYCOMPO PE 2015M | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |
| ESTOPLAST XU 150GY67 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |