Later 4 G/30-V0HF1
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Later |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Hih1W_Later-4-G-30-V0HF1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polybutylene Terephtalate (PBT). Glass fibres. UL94 V-0 classified, halogens and red phosphorous free. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.95 to 1.3 | % | |
| Flow : 2.00 mm | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 9900 | MPa | |
| 60°C | 6500 | MPa | |
| 90°C | 4100 | MPa | |
| 120°C | 3000 | MPa | |
| 150°C | 2100 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 140 | MPa | |
| Break, 60°C | 90.0 | MPa | |
| Break, 90°C | 65.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Break, 150°C | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.8 | % | |
| Break, 60°C | 2.2 | % | |
| Break, 90°C | 2.8 | % | |
| Break, 120°C | 3.0 | % | |
| Break, 150°C | 3.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 135 | °C | |
| Vicat Softening Temperature | 200 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 575 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature (2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TC 2000F | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| VESTAMID® Care ME62 | Evonik Industries AG | PEBA-Ether | VESTAMID® Care |
| NOVADURAN® 5010TRX5 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Axiall PVC 8150 White 119 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| OTECH ALLOY NT1000-80 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |