LUBMER™ LS4140
| Category: | HMWPE , High Molecular Weight Polyethylene |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | LUBMER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5GyGPp_LUBMER-LS4140.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA Alloy |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 2.00mm | 0.80 | % | ASTM D955 |
| Transverse flow : 2.00mm | 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.5 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, 23°C | 60.0 | MPa | ASTM D638 |
| Fracture, 23°C | 62.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | 150 | % | ASTM D638 |
| Flexural Modulus 3(23°C, 3.00mm, 48.0mm span) | 2200 | MPa | ASTM D790 |
| Flexural Strength 4(yield, 23°C, 3.00mm, 48.0mm span) | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 2.00 mm) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 175 | °C | ASTM D648 |
| Vicat Softening Temperature | 200 | °C | ASTM D1525 5 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.016 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Kinetic Coefficient of Friction, MCI Method, Lubmer-contact material, SUS 304, surface roughness, 6S: 0.16Critical PV value, MCI Method, Lubmer-contact material, SUS 304, surface roughness, 6S: >/= 30 MPa m/minAbrasion Loss, MCI Method, Lubmer-contact material, SUS 304, surface roughness, 6S: 30E-10 cm³/ kg-mVolume Resistivity, ASTM D257: 1E15 to 1E18 ohm-cmSpiral Flow, MCI method, 4.8mm radius: 37 cm (270°C)The values listed as Mold Shrink, Linear Flow and Trans, ASTM D955, were tested in accordance with MCI methods.Vicat Softening Point, ASTM D1525, Loading 1 (10N): >200°C |
| Note Message | |
|---|---|
| 1 . | Type 5, 50mm/min |
| 2 . | Type 5, 50mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS-361T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Tislamid® PA66 PA66 15 GFR | Tisan | Nylon 66 | Tislamid® PA66 |
| BIPEX B0420GN | Ginar Technology Co., LTD. | PBT | BIPEX |
| Hanwha Total PP BI51W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Lion Idemitsu Composites PPS V170N3 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |