| Kocetal CF302 is carbon fiber reinforced grade for high stiffness and electrical conductivity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 105 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9780 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 3.0 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, not annealed | 164 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 160 | °C | ASTM D648A |
| Melting Temperature | 166 | °C | ASTM D1525 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Nylon 1013 IU50 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| Hipolyene 6251 Y M2 | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Karina IVORY PVC COMPOUND 90901-35/ 1-D-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ Lexan_LCF1506 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Durethan® DP AKV 50 HR H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |