Order Products : sales@su-jiao.com
MAJORIS PC 9381 20 FV
| Category: | PC , Polycarbonate |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5EnGTq_MAJORIS-PC-9381-20-FV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC 9381 20 FV is a medium viscosity polycarbonate (PC) resin and contains flame retardant agent, intended for injection moulding. The product is available in natural (PC 9381 20 FV) but other colours can be provided on request They combine high mechanical requiring rigidity, thermal and electrical properties with excellent chemical resistance and dimensional stability APPLICATIONS PC 9381 20 FV is intended for the injection moulding of electrical components and mechanical systems, such as:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 11.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.28 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Injection Molded) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 5400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 143 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 134 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 34 | % | ISO 4589-2 |
| Additional Information |
|---|
| Ball Pressure Test, IEC 60695-10-2, 125°C: PassesMelt Volume-Flow Rate, ISO 1183, 300°C/1.2Kg: 8 to 14 g/10min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Flexalloy® 9604-75 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Kepamid® 1320GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| LNP™ LUBRILOY™ DX08333 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRILOY™ |
| Sylvin 8299-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Extir® VERDI PD VM A2000 AE | Versalis S.p.A. | PS (EPS) | Extir® |