LNP™ STAT-KON™ DE0039 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5DdEO2_LNPSTATKONDE0039compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DE0039 is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Flame Retardant. Also known as: LNP* STAT-KON* Compound DC-1003 FR Product reorder name: DE0039 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.30 | g/cm³ | ASTM D792 |
| -- | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.38 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.13 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9650 | MPa | ASTM D638 |
| -- | 9260 | MPa | ISO 527-2/1 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 119 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 119 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.4 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2 |
| Fracture | 2.4 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 7580 | MPa | ASTM D790 |
| -- | 8600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 145 | MPa | ASTM D790 |
| -- | 181 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 2 | 6.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 3 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 18.3 | J | ASTM D3763 |
| -- | 4.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 150 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 150 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 148 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 146 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 3.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prop 6003 | Putsch Kunststoffe GmbH | PP, Unspecified | Prop |
| Quadraflex™ ARE-93A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| SLOVAMID® 6 FRB 4 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Addisil™ 470 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Cosmic DAP D33/6120 | Cosmic Plastics, Inc. | DAP | Cosmic DAP |