| High flow ULTEM blends for thin wall application |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (345°C/10.0 kg) | 30.4 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11600 | MPa | ASTM D638 |
| Tensile Strength | |||
| Fracture 2 | 172 | MPa | ASTM D638 |
| Fracture | 171 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.6 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 9320 | MPa | ASTM D790 |
| -- 5 | 9400 | MPa | ISO 178 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 222 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 95 | J/m | ASTM D256 |
| 23°C 7 | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 204 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 8 | 209 | °C | ISO 75-2/Ae |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 150°C | 1.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 1.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 150°C | 5.5E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 23 to 150°C | 5.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 332 - 399 | °C | |
| Middle Temperature | 338 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Nozzle Temperature | 343 - 399 | °C | |
| Processing (Melt) Temp | 349 - 399 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 5720WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Gallonprene® GP420-5002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina CLEAR PVC COMPOUND 60/200 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ 2X04505 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |
| 3M™ Dyneon™ Fluoroelastomer E-20575 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |