ACLAR® UltRx 3000
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5D6Tsl_ACLAR-UltRx-3000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Aclar UltRx 3000 is a 3.00 mil CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment and provides the best barrier of any clear film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.11 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 100 µm | 1170 | MPa | ASTM D882 |
| TD : 100 µm | 1170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 100 µm | 51.7 | MPa | ASTM D882 |
| TD : Yield, 100 µm | 39.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 100 µm | 200 | % | ASTM D882 |
| TD : Yield, 100 µm | 250 | % | ASTM D882 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 76 µm, 40°C, 75% RH | 0.077 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 76 µm, 38°C, 100% RH | 0.090 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 76 µm, 25°C, 60% RH | 0.016 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 76 µm, 30°C, 60% RH | 0.023 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 211 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (102 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 6.23 m²/kgTensile Strength @ Yld, ASTM D882, MD, 4 mil: 6000 to 9000 psiTensile Strength @ Yld, ASTM D882, TD, 4 mil: 4500 to 7500 psiTensile Elongation @ Yield, ASTM D882, MD, 4 mil: 150 to 250%Tensile Elongation @ Yield, ASTM D882, TD, 4 mil: 200 to 300%Secant Modulus, ASTM D882, 4 mil, MD & TD: 160000 to 200000Tear Strength, ASTM D1004, Graves MD: 325 to 375 g/milTear Strength, ASTM D1004, Graves TD: 275 to 325 g/milCrystalline Melting Point, ASTM D4591: 211 °CDimensional Stability, ASTM D1204, MD: +5 to +10 %Dimensional Stability, ASTM D1204, TD: -5 to -10 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen S33LS | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| APEX® 1586 | Teknor Apex Company | PVC, Flexible | APEX® |
| Artenius UNIQUE G25 | Artenius | PET | Artenius |
| LNP™ STAT-KON™ DX96717C compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| TechnoElast S A8008 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |