TAROMID A 280 G6 MB1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Cvzv9_TAROMID-A-280-G6-MB1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROMID A 280 G6 MB1 is a polyamide 66 (nylon 66) product containing a 30% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/1.0 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow | 0.90 - 1.1 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.75 | % | ASTM D570, ISO 62 |
| Saturation | 5.0 | % | ASTM D570 |
| Saturated, 23°C | 5.0 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 170 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8200 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 240 | MPa | ISO 178 |
| Fracture | 240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.8 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 244 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | 100 | °C | ASTM D794 |
| Vicat Softening Temperature | 254 | °C | ISO 306/B50, ASTM D1525 1 |
| Melting Temperature | 256 | °C | |
| CLTE - Flow (-30 to 30°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 26 | % | ASTM D2863 |
| Additional Information |
|---|
| Granule Humidity, TARO 002: <0.15%Spiral Flow, TARO 003, 280°C - 60°C: 320Ball Pressure Test, VDE 0470: 165°CContinuous Service Temperature, IEC 216, 130 hr: 100°CContinuous Service Temperature, IEC 216, 180 hr, short term: 140°CDensity, ISO 118: 1.36 to 1.38 Mg/m³Density. ASTM D792: 1.36 to 1.38 Mg/m³Notched Izod Impact Strength , ISO 180, 23°C: 110 J/mCharpy Impact Strength, ASTM D256, 23°C, 4mm: 7.8 kJ/m² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 - 90.0 | °C | |
| Pre-drying equipment | 80.0 - 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-drying equipment | 3.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Shinko-Lac® ASA S351 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Sylvin 2900-93 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| APEX® 3300-68NT | Teknor Apex Company | PVC, Flexible | APEX® |
| LNP™ LUBRICOMP™ RFP36 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |