NEO-ZEX™ 2540R
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Prime Polymer Co., Ltd. |
| Trademark: | NEO-ZEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5CtGZ2_NEO-ZEX-2540R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NEO-ZEX™ 2540R is a Linear Low Density Polyethylene product. It can be processed by rotational molding and is available in Asia Pacific, Europe, or North America. Applications of NEO-ZEX™ 2540R include containers and plumbing/piping/potable water. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.4 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 57 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 11.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 470 | % | ISO 527-2 |
| Flexural Modulus | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 101 | °C | ISO 306 |
| Melting Temperature | 121 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niche PPCT40BK | Niche Polymer, LLC | PP Copolymer | Niche |
| Karina CRYSTAL PVC COMP. E 75/325-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Braskem PE PROXESS 2606 | Braskem | LLDPE | Braskem PE |
| POCAN® AF 4130 000000 | LANXESS GmbH | PBT+ASA | POCAN® |
| Zetpol® 2010H | Zeon Corporation | NBR | Zetpol® |