INSTRUC PPSGF15
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5CgMTF_INSTRUC-PPSGF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% GLASS FIBER REI FORCED POLYPOLYPHPHE YLE E SULFIDE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 93.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact | 160 to 270 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 321 to 332 | °C | |
| Mold Temperature | 135 to 177 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 7.6E-3 to 0.013 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2105 HF | RTP Company | PEI | RTP |
| SLOVAMID® 6 GF 20 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Dutral® CO 054 | Versalis S.p.A. | EPDM | Dutral® |
| Generic Nylon 66 - Glass\Carbon Fiber | Generic | Nylon 66 | Generic |
| ESTOPLAST PP 3025WW01 | Ester Industries Ltd. | PP, Unspecified | ESTOPLAST PP |