Braskem PE LD7001A
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5BhVW7_Braskem-PE-LD7001A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LD7001A is a Low Density Polyethylene produced by High Pressure Process, in Autoclave reactor. Developed for the manufacturing of extruded films. It has high mechanical and impact strength, good processability, high ESCR and good shrinkage. Additivation:
Application: Coextruded and shrink films. Process: Recommended processing conditions for film extrusion about 200 - 220 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.34 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm | 30.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 280 | % | ASTM D882 |
| TD : Fracture, 38 µm | 880 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm) | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (38 µm) | 130 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm) | 61 | ASTM D2457 | |
| Haze | 19 | % | ASTM D1003 |
| Injection instructions |
|---|
| Recommended Coextrusion Conditions: Temperature Profile: 200°C to 220°C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® HHM TR-257 | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Shinko-Lac® ASA S610 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Unipren® Elastomers A3 PRTA010 45A EG06S1 UP326 | Petropol Industry and Trade of Polymers LTDA | TPE | Unipren® Elastomers |
| AKROMID® B3 GF 30 S1 natural (1383) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Sylvin 8225-80FR Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |