HiPrene® HSG43HT
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5Ar6Ok_HiPrene-HSG43HT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® HSG43HT is a glass fiber filled polypropylene compound suitable for injection moulding. This material excellent Long-Term Thermal Stability and combines good stiffness, good processability and surface finish. It has been developed especially for Automotive applications where high heat resistance is necessary. This material is available in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 3.5 | g/10 min | ISO 1133 |
| Ash Content (600°C) | 30 | % | ISO 3451 |
| Volatile Matter | 0.12 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.5 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 6000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | kJ/m² | ISO 179/1eA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 4.00 - 6.50 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumInjection Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2008N0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| McCann PP M40CCPP10 | McCann Plastics Inc. | PP Copolymer | McCann PP |
| Roscom PVC 600-95/96 | Roscom, Inc. | PVC, Flexible | Roscom PVC |
| Tarnoform® 200 G2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Karina COMP. PVC BLACK -E KAPU 601-48/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |