Karina WHITE PVC COMPOUND E-844-10/219-Y-ERYM
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5AfnK8_Karina-WHITE-PVC-COMPOUND-E-844-10-219-Y-ERYM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TIN STABILIZED PVC COMPOUND RECOMMENDED FOR EXTRUSION OF PROFILES FOR GENERAL APPLICATIONS. IT IS SUPPLIED IN PELLET FORM AND SHOULD BE PROCESSED AT THE TEMPERATURE RANGE OF 170C TO 190C. |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.44 to 1.50 | g/cm³ | ASTM D792 |
| Color a | -1.70 to -0.100 | ME 12 | |
| Color b | -5.07 to -3.47 | ME 12 | |
| Color L | 89.6 to 91.2 | ME 12 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | > 75 | °C | ASTM D648 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Torque | 35.0 | ME 37 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 78 to 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 39.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 70 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 130 | J/m | ASTM D256A |
| Reverse Notch Izod Impact | 63 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 81.0 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ferro PP LPP35BC69GY | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hyundai EP Breathable AT880H/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |
| LNP™ LUBRICOMP™ RA004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| POCAN® B 1505 000000 | LANXESS GmbH | PBT | POCAN® |
| SQUARE® SCR2530-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |