Hifax CA 7201 A
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 59GoY7_Hifax-CA-7201-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hifax CA 7201 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell' s proprietary Catalloy process technology. It is primarily used for bumper and interior/exterior trim applications in Automotive. It has a very high impact performance, reduced shrinkage and a very good paintability. The material also has a high level of processability. The grade is available in natural pellet form. For regulatory compliance information see Hifax CA 7201 A Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.2 | % | |
| Flow | 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 56 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 17.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 500 | % | ISO 527-2 |
| Flexural Modulus - Chord 1(23°C) | 750 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 14 | kJ/m² | |
| -30°C | 44 | kJ/m² | |
| -20°C | No Break | ||
| 23°C | 50 | kJ/m² | |
| Instrumented Dart Impact 2(-30°C, 3.20 mm, Energy at Peak Load, Ductile Failure) | 23.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 45.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | ISO 306/A50 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 3070 | Teknor Apex Company | PVC, Flexible | APEX® |
| Axiall PVC 8705 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Celstran® PP-GF30-02 AF 3001 | Celanese Corporation | PP, Unspecified | Celstran® |
| Geon™ Duracap™ L4605 Red 7640 | PolyOne Corporation | PVC, Semi-Rigid | Geon™ Duracap™ |
| Sylvin 4240-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |