EPLAMID 6 GFR 5 NC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 58neBT_EPLAMID-6-GFR-5-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6, reinforced with 5% of glass fiber, heat stabilized, lubricated for injection moulding. Eplamid 6 GFR 5 is used in all sectors of industry, offering a perfect balance of thermal and mechanical properties. This material is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.0 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.70 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 5.0 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 81 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3200 | 2600 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 85.0 | 65.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 4.0 | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 3000 | 2300 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 145 | 130 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 7.0 | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3(0.45 MPa, Unannealed) | 185 | -- | °C | ISO 75-2/B |
| Vicat Softening Temperature | 195 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 215 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® HI 0302 | Plastic Solutions, Inc. | PS (HIPS) | PrimaFlex® |
| RTP ESD A 4080 | RTP Company | PPA | RTP |
| RAMTAL PMH2017 | Polyram Ram-On Industries | Acetal (POM) Homopolymer | RAMTAL |
| Moplen EP2838 | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Sylvin 5143-88 Red 6177 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |