Softflex® 7088 Datasheet,TPE Alloy,Network Polymers, Inc.-SHANGHAI SUSHENG

Message
Softflex®7088 is a thermoplastic elastomer alloy (TPE alloy) product,. It is available in North America. Typical application areas are: engineering/industrial accessories. The main characteristics are: chemical resistance.

General Information
Features	Good coloring Good chemical resistance
Uses	overmolding

Physical	Nominal Value	Unit	Test Method
Density (Natural)	0.890	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	70		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength ¹(Break, 23°C, 3.18 mm)	10.5	MPa	ASTM D412
Tensile Elongation ²(Break, 23°C, 3.18 mm)	800	%	ASTM D412

Additional Information
Processing Information: Injection Molding (preferable standard 2-component injection molding machine to get adhesion to substrate)Purging: Purge thoroughly before and after use of this product (e.g. polypropylene with MFI between 0.5 - 2.5)Drying Time: Material is not hygroscopic and drying is only necessary if material is stored under moisture.Shrinkage Properties: This material is anisotropic. The shrinkage properties are higher in the flow direction, and the shrinkage in the cross-flow direction is less. Typical shrinkage properties values are between 0.8 - 2.2%Rheoligical Properties: This material is shear dependent. Viscosity will decrease at higher shear rates, and should be considered during injection molding design and setup of processing conditions.FDA Compliance: Softflex 7088 is based on Styrenic-Ethylene/Bthylene block-copolymers as described by FDA, article 21. A valid Code of Federal Regulations (CFR) is described in paragraph 177.1810 and/or paragraph 176.170, categories I, II, IV-B, VI, VII-B, VIII in panel 1.

Additional Information

Processing Information: Injection Molding (preferable standard 2-component injection molding machine to get adhesion to substrate)Purging: Purge thoroughly before and after use of this product (e.g. polypropylene with MFI between 0.5 - 2.5)Drying Time: Material is not hygroscopic and drying is only necessary if material is stored under moisture.Shrinkage Properties: This material is anisotropic. The shrinkage properties are higher in the flow direction, and the shrinkage in the cross-flow direction is less. Typical shrinkage properties values are between 0.8 - 2.2%Rheoligical Properties: This material is shear dependent. Viscosity will decrease at higher shear rates, and should be considered during injection molding design and setup of processing conditions.FDA Compliance: Softflex 7088 is based on Styrenic-Ethylene/Bthylene block-copolymers as described by FDA, article 21. A valid Code of Federal Regulations (CFR) is described in paragraph 177.1810 and/or paragraph 176.170, categories I, II, IV-B, VI, VII-B, VIII in panel 1.

Injection	Nominal Value	Unit
Rear Temperature	160 - 185	°C
Front Temperature	180 - 207	°C
Nozzle Temperature	207 - 232	°C
Mold Temperature	29.4 - 65.6	°C

Note Message
1 .	510 mm/min
2 .	510 mm/min

Resin Grade	Manufacturer	Category	Trademark
Queo™ 8210	Borealis AG	Plastomer	Queo™
Abstron IMGS 20	Bhansali Engineering Polymers Limited	SAN	Abstron
ALTECH® PA66 A 2030/106 GF30	ALBIS PLASTIC GmbH	Nylon 66	ALTECH® PA66
Geon™ Bold L5801	PolyOne Corporation	PVC Alloy	Geon™ Bold
Karina WHITE PVC COMPOUND -E 854-10/150-ERYB	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina

Category:	TPE Alloy , Thermoplastic Elastomer Alloy
Manufacturer:	Network Polymers, Inc.
Trademark:	Softflex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	57uZ7s_Softflex-7088.pdf
PRICE:	Order Products email sales@su-jiao.com