Latistat 62-06 K/10
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latistat |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 57ZFYx_Latistat-62-06-K-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dissipative product based on Polyamide 6 (PA 6). Carbon fibre. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.1 to 1.4 | % | |
| Flow : 2.00 mm | 0.40 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 8100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 115 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 3.5 | % | |
| Break, 23°C | 7.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 120 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 51 T 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| NEXUS PE HDPE-00649 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| ACCUTECH™ HP0339W40L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Geon™ Vinyl Flexible B8502 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LubriOne™ NN-30GF/13T-2S Black | PolyOne Corporation | Nylon 66 | LubriOne™ |