Lupox® GP2150
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 57M5Gu_Lupox-GP2150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose Application IT/OA, E&E, Automotive (Connector) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 93.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4900 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 210 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 205 | °C | |
| Peak Melting Temperature | 223 | °C | ASTM D3418 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 25 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) 5 | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | HB | ||
| 1.50 mm | HB | ||
| 3.30 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 235 to 250 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 245 to 255 | °C | |
| Nozzle Temperature | 245 to 255 | °C | |
| Processing (Melt) Temp | 245 to 255 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PC 1008 schwarz | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| CONAP® CE-1171 | Cytec Industries Inc. | Acrylic, Unspecified | CONAP® |
| Comai 712-1 UV | Comai Ltda | PP, Unspecified | Comai |
| OmniTech™ PBT GR17 FR0 | OMNI Plastics, LLC | PBT | OmniTech™ |
| Sylvin 4200-68 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |