Zytel® 70G13L NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 556XDl_Zytel-70G13L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 13% Glass Reinforced Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.23 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.70 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.7 | -- | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 7.6 | -- | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.2 | -- | % | ISO 62 |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 13 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 3300 | MPa | |
| 1000 hr | -- | 2200 | MPa | |
| Flexural Modulus | 4800 | 2900 | MPa | ISO 178 |
| Flexural Stress | 190 | 100 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 4.5 | 4.0 | kJ/m² | |
| -30°C | 4.5 | 4.0 | kJ/m² | |
| 23°C | 5.0 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 40 | 30 | kJ/m² | |
| 23°C | 40 | 70 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 4.5 | 3.0 | kJ/m² | |
| -30°C | 4.5 | 3.0 | kJ/m² | |
| 23°C | 4.5 | 4.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 35 | 28 | kJ/m² | |
| 23°C | 40 | 55 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 238 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.0E-5 | -- | cm/cm/°C | |
| Transverse | 9.6E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 25 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.90 | -- | ||
| 1 MHz | 3.20 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.013 | -- | ||
| 1 MHz | 0.015 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 27 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.710 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 24 | -- | % | ISO 4589-2 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 6.00 | -- | µgC/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cri-Line LC-615-65-LV | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Fainplast PVC MGS 86 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Formolene® L42022B | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| LNP™ LUBRICOMP™ UCP36S compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |
| TECHNYL® C 216 V55 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |