Electrafil® J-3/CF/30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 53sUPa_Electrafil-J-3-CF-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®J-3/CF/30 is a polyamide 6 (nylon 6) product, which contains a 30% carbon fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Electrafil®The application fields of J-3/CF/30 include packaging, engineering/industrial accessories, automobile industry, commercial/office supplies and conveyor belts. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 19300 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 207 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.3 | % | ASTM D638 |
| Flexural Modulus (23°C) | 17200 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 317 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 213 | °C | ASTM D648 |
| CLTE - Flow | 1.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.5E+2 | ohms | ASTM D257 |
| Volume Resistivity | 5.5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D4496: 1E2-1E3 ohmsVolume Resistivity, ASTM C611: 1-10 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 277 - 288 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Nozzle Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 79.4 - 104 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toler EVA 40028 | Toler Chemical, Inc | EVA | Toler EVA |
| Nipolon® Hard 4010 | TOSOH Corporation | HDPE | Nipolon® Hard |
| AKROMID® A3 GF 60 1 black (2395) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Kepamid® 2330GFS | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| Karina GREEN PVC COMP. -E 850-40/174-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |