EPIMIX POM CBR 25 NC
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPIMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 51cxRT_EPIMIX-POM-CBR-25-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYACETAL POM, reinforced with 25% of glass bead, Standard-flow grad, for injection molding. POLYACETAL POM , is used in all sectors of industry, compliance with RoHs derivatives. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.55 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 4.00 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.3 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.90 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | -- | % | ISO 62 |
| Ash Content | 25 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 80 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 2800 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 40.0 | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 12 | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2850 | 2700 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 74.0 | 63.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 5.0 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 6.0 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 105 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 160 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 160 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J704UG | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| Sumiflex® QE QE144ATH | Mitsubishi Chemical Corporation | TES | Sumiflex® QE |
| Moplen HP500D | LyondellBasell Industries | PP Homopolymer | Moplen |
| Adell Polyamide AR-34 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Ketjenflex® 9S | Axcentive SARL | Plasticizer | Ketjenflex® |